Synthesis and characterization of irradiated injectable bone substitute paste based on hydroxyapatite

Synthesis and characterization of hydroxyapatite, chitosan and hydroxypropyl methylcellulose (HPMC) composite in injectable paste form have been done. The composite was synthesized by stirring hydroxyapatite, chitosan and HPMC until homogen. IBS paste was irradiated at the dose of 25 kGy (sterile dose). Characterization of IBS paste was conducted by measuring of the water content, identification of functional group with Fourier Transform Infra Red Spectrophotometer (FTIR), and identification of sample morphology with Scanning Electron Microscope Energy Dispersive Spectrophotometer (SEM EDS). The result showed that the water content of irradiated sample was higher than unirradiated sample due to water radiolysis. Several specific bands of IBS paste were identified, i.e., carbonate (CO₃ ^2-), at 1420 cm^-1 , phosphate (PO₄^3-) at 1043 cm^-1, 605 cm^-1, 568 cm^-1 and chitosan (NH₂) at 1599 cm^-1. There is no significant difference in absorbed band between irradiated and unirradiated samples. IBS paste has a microstructure with the size of 0.05 – 0.1 μm. Electron beam irradiation did not change the structure and morphology of sample. (author)