Characterization of titanium chromium nitride nanocomposite protective coatings

The structural, chemical, optical and mechanical properties of titanium chromium nitride nanocrystalline films deposited by ion beam-assisted deposition were studied by means of X-ray diffraction, X-ray photoelectron spectroscopy, spectroscopic ellipsometry, nanoindentation and wear testing. Coatings were deposited on silicon and stainless steel substrates with growth temperatures of 150 and 400 deg. C. The concentration of titanium and chromium in the film was regulated by controlling their evaporation rates. The nitrogen concentration was controlled by varying the nitrogen ion current. X-ray diffraction and X-ray photoelectron spectroscopy measurements indicated that the films deposited at 150 deg. C formed solid solutions whereas those produced at 400 deg. C formed nanocomposites. The optical constants were measured using spectroscopic ellipsometry. A correlation between the elemental/phase composition and optical constants was established. The mechanical properties of the coatings were evaluated using nanohardness testing and were found to depend on composition. The nanocomposite films were the hardest (hardness of 30 GPa and elastic modulus of 300 GPa). Tribological properties of titanium chromium nitride coated 440 C stainless steel coupons were evaluated using a ball-on-disk tribometer. These tests were conducted under a load of 50 N for 1.5 million cycles at 180 rpm. Coatings deposited at high temperature did not show any signs of wear