The electrochemical- and high temperature behaviour of uranium-lanthanide-mixed oxides

Creators

Description

By using X-ray diffraction and electrochemical techniques, the phase diagram of the system PrO1,5-UO2-O2 has been established for the temperature-region from 1073 to 1573 K. The data obtained have been used to describe a defect structure model. The following phases were detected in this system: U3O8, which shows no solubility for PrO1,5, a fluorite phase; a rhomboedral phase, UO3 x 6 PrO1,5, a C-typ phase with small solubility of UO2+x in PrO1,5. A new developed galvanic cell has been used to perform the electrochemical measurements. The data obtained with this technique were used to define the regions of sub- and superstoichiometry. The solubility of the two components in each other is determined by the component wich has the higher oxygen partial pressure. Thermodynamic data were derived from the electrochemical measurements. The components and phases investigated in this way comprise the PrO1,5-, UO2-range, together with the substoichiometric compounds (Pr0,4U0,6) O1,95, PrUO3,50, (Pr0,77U0,33) O1,89, (UO3 x 6 PrO1,5). (orig.)

Availability note (English)

MF available from INIS under the Report Number.

Abstract (German)

Unter Verwendung roentgenographischer- und elektrochemischer Methoden wurde das Phasendiagram des Systems PrO1,5-U2-O2 im Temperaturbereich von 1073 bis 1573 K ermittelt. Die erhaltenen Werte wurden zur Beschreibung eines Strukturmodells verwendet. Die folgenden Phasen wurden in diesem System bestimmt. U3O8, das keine Loeslichkeit fuer PrO1,5 aufweist, eine Fluorit-Phase; eine rhomboedrische Phase; UO3 x 6 PrO1,5, eine C-Typ-Phase mit geringer Loeslichkeit von UO2+x in PrO1,5. Eine neu entwickelte galvanische Zelle wurde zur elektrochemischen Messung verwendet. Die mit dieser Technik erhaltenen Werte wurden zur Definition unter- und ueberstoechiometrischer Gebiete verwendet. Die Loeslichkeit der beiden Komponenten ineinander wird durch die Komponente mit dem hoeheren Sauerstoffpartialdruck bestimmt. Thermodynamische Werte wurden aus den elektrochemischen Messungen abgeleitet. Die auf diese Weise bestimmten Komponenten und Phasen enthalten das PrO1,5-UO2-Gebiet, zusammen mit den unterstoechiometrischen Verbindungen (PrO0,4U0,6) O1,95, PrUO3,50, (Pr0,77U0,33) O1,89, (UO3 x 6 PrO1,5). (orig.)

Files

Restricted

The record is publicly accessible, but files are restricted to users with access.

Additional details

Additional titles

Original title (German)
Das elektrochemische- und Hochtemperaturverhalten von Uran-Lanthaniden-Mischoxiden

Publishing Information

Imprint Pagination
110 p.
Report number
KFK--2518

INIS

Country of Publication
Germany
Country of Input or Organization
Germany
INIS RN
10422907
Subject category
S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; S75: CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY;
Resource subtype / Literary indicator
Thesis
Descriptors DEI
CHEMICAL COMPOSITION; CRYSTAL DEFECTS; CRYSTAL MODELS; ELECTROCHEMISTRY; ELECTROMOTIVE FORCE; MEASURING METHODS; PHASE DIAGRAMS; PHASE STUDIES; PRASEODYMIUM OXIDES; SOLID SOLUTIONS; SOLIDS; SUBSTOICHIOMETRY; TEMPERATURE DEPENDENCE; THERMODYNAMIC PROPERTIES; URANIUM OXIDES; VERY HIGH TEMPERATURE
Descriptors DEC
ACTINIDE COMPOUNDS; CHALCOGENIDES; CRYSTAL STRUCTURE; DIAGRAMS; DISPERSIONS; ELECTRIC POTENTIAL; HOMOGENEOUS MIXTURES; INFORMATION; MATHEMATICAL MODELS; MIXTURES; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; PRASEODYMIUM COMPOUNDS; RARE EARTH COMPOUNDS; SOLUTIONS; URANIUM COMPOUNDS