Effect of Pr2O3 and Dy2O3 on viscosity, electric conductivity and surface properties of bismuth oxide

Creators

  • 1. Inst. Metallurgii UrO RAN, Ekaterinburg (Russian Federation)

Description

Surface tension, viscosity and electric conductivity are studied for Bi2O3-Pr2O3 and Bi2O3-Dy2O3 melts with 0, 5, 10, 15 and 20 mol % of the second component. Contact interaction of the melts with Pt and a Pt + 10% Rh alloy is also studied. It is stated that a Pr2O3 content increase results in a rise of activation energy of viscous flow both in low and high temperature ranges. Electric conductivity curve displays a minimum at praseodymium oxide concentration of 5 mol %. As the content of Dy2O3 increases the viscosity reduces. A rather strong interaction is observed between all melts studied and Pt and Pt + 10% Rh substrates

Abstract (Russian)

Проведено исследование вязкости, электропроводности и поверхностного натяжения расплавов Bi2O3-Pr2O3 и Bi2O3-Dy2O3, содержащих 0, 5, 10, 15 и 20 мол. % второго компонента. Изучено контактное взаимодействие этих расплавов с Pt и сплавом Pt + 10% Rh. Установлено, что с ростом концентрации Pr2O3 энергия активации вязкого течения увеличивается как для низко-, так и для высокотемпературных областей. Значения электропроводности проходят через минимум при содержании в расплаве 5 мол. % оксида празеодима. По мере роста концентрации Dy2O3 вязкость увеличивается, а электропроводность снижается. Отмечено достаточное сильное взаимодейсвтие расплавов всех изученных составов с подложками из Pt и Pt + 10% Rh

Additional details

Additional titles

Original title (Russian)
Влияние Пр

Publishing Information

Journal Title
Rasplavy
Journal Issue
no.1
Journal Page Range
p. 3-7
ISSN
0235-0106
CODEN
RASPEM

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
31035484
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
BISMUTH OXIDES; CONCENTRATION RATIO; DYSPROSIUM OXIDES; ELECTRIC CONDUCTIVITY; PLATINUM; PLATINUM BASE ALLOYS; PRASEODYMIUM OXIDES; RHODIUM ALLOYS; SUBSTRATES; SURFACE TENSION; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 1000-4000 K; VISCOSITY; WETTABILITY
Descriptors DEC
ALLOYS; BISMUTH COMPOUNDS; CHALCOGENIDES; DYSPROSIUM COMPOUNDS; ELECTRICAL PROPERTIES; ELEMENTS; METALS; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; PLATINUM ALLOYS; PLATINUM METAL ALLOYS; PLATINUM METALS; PRASEODYMIUM COMPOUNDS; RARE EARTH COMPOUNDS; SURFACE PROPERTIES; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENTS

Optional Information

Notes
9 refs.; 2 tabs.; 2 figs.