Using of microspecimens for evaluation of the remaining life of the reactor equipment and pipes
- 1. Zaporozhskaya AEhS, Ehnergodar (Ukraine)
- 2. NNTs KhFTI, Khar'kov (Ukraine)
Description
Mechanical properties and structure of base metal of a main circulation pipeline of steel 10GN2MFA are studied both in initial state and after operation in power units No. 1 and No. 2 of the South Ukrainian NPP and the Zaporozhe-1 reactor (WWER-1000). It is revealed that steel 10GN2MFA operation for 100 thousand h results in an increases of yield strength by 10-15% and in a decrease of ductility and fracture toughness by 10-15%. Mechanical tests are performed using standard specimens and microspecimens with the aim to establish the correlation between their properties. The obtained results are analyzed; recommendations are given on the use of microspecimens to control mechanical properties and structure of the metal of main equipment and pipelines of NPP units
Abstract (Russian)
Исследованы механические свойства и структура основного металла главного циркуляционного трубопровода из стали 10ГН2МФА в исходном состоянии и после эксплуатации на энергоблоках ном. 1 и ном. 2 Южно-Украинской АЭС и энергоблока ном. 1 Запорожской АЭС (ВВЭР-1000). Установлено, что эксплуатация стали 10ГН2МФА в течение 100 тыс. ч приводит к увеличению предела текучести на 10-15% и снижению пластичности и ударной вязкости на 10-15%. Механические испытания проводили на стандартных образцах и микрообразцах с целью установления корреляции между их свойствами. Проведен анализ полученных результатов, даны рекомендации по использованию микрообразцов для контроля механических свойств и структуры металла основного оборудования и трубопроводов энергоблоков АЭСAdditional details
Additional titles
- Original title (Russian)
- Использование микрообразцов для оценки остаточного ресурса оборудования и трубопроводов реакторов VVEhR
Publishing Information
- Journal Title
- Metallovedenie i Termicheskaya Obrabotka Metallov
- Journal Issue
- no.12
- Journal Page Range
- p. 31-35
- ISSN
- 0026-0819
- CODEN
- MTOMAX
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 35081186
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- FRACTURE PROPERTIES; LOW ALLOY STEELS; PIPELINES; SOUTH UKRAINIAN-1 REACTOR; SOUTH UKRAINIAN-2 REACTOR; TEMPERATURE RANGE 0273-0400 K; TEMPERATURE RANGE 0400-1000 K; TENSILE PROPERTIES; ULTIMATE STRENGTH; YIELD STRENGTH; ZAPOROZHE-1 REACTOR
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; ENRICHED URANIUM REACTORS; IRON ALLOYS; IRON BASE ALLOYS; MECHANICAL PROPERTIES; POWER REACTORS; PWR TYPE REACTORS; REACTORS; STEELS; TEMPERATURE RANGE; THERMAL REACTORS; TRANSITION ELEMENT ALLOYS; WATER COOLED REACTORS; WATER MODERATED REACTORS; WWER TYPE REACTORS
Optional Information
- Notes
- 13 refs., 4 tabs.