Phase stability, microstructure and high-temperature properties of NbSi₂- and TaSi₂-oxide conducting ceramic composites

NbSi₂- and TaSi₂-based electroconductive ceramic composites with the addition of 40–70 vol% Al₂O₃ and ZrO₂ particles were fabricated by high-temperature sintering (1400–1600 °C) under argon. Their phase stability, microstructural evolution, oxidation kinetics and electrical properties were studied at high temperatures. The densification of the composites was improved by increasing the oxide phase content and sintering temperature. The interaction of the starting metal disilicides with residual oxygen sources resulted in the formation of the hexagonal-structured 5–3 metal silicide (Nb₅Si₃ and Ta₅Si₃) phases. The increasing sintering temperature and volume percentage of the oxide phase reduced the pest oxidation, particularly for the silicide–alumina composites, which exhibited lower oxidation-induced mass changes than their dense monolithic metal silicides. Depending on the silicide–oxide volume percentage, their electrical conductivities ranged from 5.3 to 111.3 S/cm at 900 °C. Their phase stability, reduced oxidation rates and high electrical conductivities at high temperatures show promise for future high-temperature applications in advanced sensing.