Intercalation of ceramic high-temperature superconductors
Description
The dissertation describes the preparation of Bi2Sr2CaCu2O8+δ, the resulting structural consequences, and the changes in the physical properties due to intercalation. X-ray diffraction studies show three structural consequences of intercalation with iodine: First, there is a dramatic 23 percent increase in the interblock copper oxide plane distance in the c-lattice constants of Bi2Sr2CaCu2O8+δ. Secondly, the staggered configuration of neighbouring halves of elementary cells is changed into an eclipsed conformation, by which the symmetry of the crystal lattice is enhanced and the elementary cells are more or less halved. Thirdly, structural faults are introduced into the crystal lattice, as is indicated especially by a comparison of Rocking curves prior to intercalation and after intercalation. The intercalation of Bi2Sr2CaCu2O8+δ leads to a Tc reduction of about 10 K. (orig./MM)
Abstract (German)
Die Arbeit beschaeftigt sich mit der Praeparation von, mit Iod interkaliertem Bi2Sr2CaCu2O8+δ, den damit verbundenen strukturellen Konsequenzen und den Aenderungen physikalischer Eigenschaften durch die Interkalation. Roentgenbeugungsuntersuchungen zeigen, dass die Interkalation mit Iod drei strukturelle Konsequenzen fuer die Wirtsstruktur zur Folge hat. Erstens beobachtet man eine dramatische Vergroesserung des Interblock-Kuferoxid-Ebenen Abstandes um 23 Prozent der c-Gitterkonstanten von Bi2Sr2CaCu2O8+δ. Zweitens wird die 'staggered' Anordnung direkt benachbarter Elementarzellenhaelften in eine 'eclipsed' Konformation ueberfuehrt. Dadurch wird die Symmetrie des Kristallgitters erhoeht und die Elementarzelle in etwa halbiert. Als dritte Folge der Interkalation werden strukturelle Stoerungen in das Kristallgitter eingefuehrt, worauf insbesondere der Vergleich von Rocking-Kurven vor und nach der Interkalation hindeutet. Die Interkalation von Bi2Sr2CaCu2O8+δ mit Iod fuehrt zu einer Tc-Verkleinerung von ca. 10 K. (orig./MM)Additional details
Additional titles
- Original title (German)
- Interkalation von keramischen Hochtemperatur-Supraleitern
Publishing Information
- Publisher
- Shaker.
- Imprint Place
- Aachen (Germany)
- ISBN
- 3-8265-0750-9
- Imprint Pagination
- 119 p.
- Series
- Berichte aus der Physik.
- ISSN
- 0945-0963
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 27024839
- Subject category
- S75: CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY;
- Descriptors DEI
- BISMUTH OXIDES; CALCIUM OXIDES; CLATHRATES; COPPER OXIDES; ELECTRIC CONDUCTIVITY; HIGH-TC SUPERCONDUCTORS; IODINE; STOICHIOMETRY; STRONTIUM OXIDES; X-RAY DIFFRACTION
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; BISMUTH COMPOUNDS; CALCIUM COMPOUNDS; CHALCOGENIDES; COHERENT SCATTERING; COPPER COMPOUNDS; DIFFRACTION; ELECTRICAL PROPERTIES; ELEMENTS; HALOGENS; NONMETALS; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; SCATTERING; STRONTIUM COMPOUNDS; SUPERCONDUCTORS; TRANSITION ELEMENT COMPOUNDS