Vitrification testing of simulated high-level radioactive waste from Hanford

The Hanford Waste Vitrification Plant may apply vitrification technology, being developed at Pacific Northwest Laboratory, to solidify selected Hanford waste streams prior to disposal in a federal repository. Based on the first stage of flowsheet development and laboratory testing, a reference working glass and two candidate simulated feed slurries were recommended for vitrification testing. Over 500 hours of melter testing were performed in 1985 during prototype vitrification experiments. Testing demonstrated that the slurry compositions had acceptable processing characteristics in a ceramic melter. A pro-made glass former frit was determined to be preferred as the method of glass-former addition. Due to a high chromium content in the waste, spinel crystal formation and settling occurred in the glass tank. The nature and extent of off-gas effluents were consistent with past experiments processing slurries containing formic acid