Surface modification of cadmium sulfide thin film honey comb nanostructures: Effect of in situ tin doping using chemical bath deposition

Graphical abstract: - Highlights: • Novel honey comb like cadmium sulfide thin film nanostructures prepared using chemical bath deposition on glass substrates. • Honey comb nanostructure found in two layers: an ultra thin film at bottom and well inter connected with walls of < 25 nm thick on top; hence maximum surface area possible for CdS nanostructure. • Shell size of the nanostructures and energy band gaps were controlled also an enhanced persistent conductivity observed on Sn doping. - Abstract: Even though nanostructures possess large surface to volume ratio compared to their thin film counterpart, the complicated procedure that demands for the deposition on a substrate kept them back foot in device fabrication techniques. In this work, a honey comb like cadmium sulfide (CdS) thin films nanostructure are deposited on glass substrates using simple chemical bath deposition technique at 65 °C. Energy band gaps, film thickness and shell size of the honey comb nanostructures are successfully controlled using tin (Sn) doping and number of shells per unit area is found to be maximum for 5% Sn doped (in the reaction mixture) sample. X-ray diffraction and optical absorption analysis showed that cadmium sulfide and cadmium hydroxide coexist in the samples. TEM measurements showed that CdS nanostructures are embedded in cadmium hydroxide just like "plum pudding". Persistent photoconductivity measurements of the samples are also carried out. The decay constants found to be increased with increases in Sn doping.