Study of irradiation induced surface pattern and structural changes in Inconel 718 alloy

Helium ions irradiation induced surface pattern and structural changes of Inconel 718 alloy were studied with the combined utilization of atomic force microscopy (AFM), x-ray diffraction (XRD) and transmission electron microscopy (TEM). In addition, SRIM-2013 software was used to calculate the sputtering yield and detailed collision events. The result shows that, irradiation dose play an important role in altering the pattern of the surface. Enhanced irradiation aggravated the surface etching and increased the surface roughness. In ion irradiated layer, large amount of interstitials, vacancies and defect sinks were produced. Moreover, in samples with increasing dose irradiation, the dependence of interplanar spacing variation due to point defects clustering on sink density was discussed. (paper)