Luminescence spectroscopy of Eu³⁺ and Mn²⁺ ions in MgGa₂O₄ spinel

Photoluminescence and excitation spectra of the spinel-type MgGa₂O₄ with 0.5 mol. % Mn²⁺ ions and Eu³⁺ content from 0 to 8 mol. % have been investigated in this work at room temperature. Polycrystalline samples were synthesized via high-temperature solid-state reaction method. Photoluminescence spectra of all samples exhibit host emission presented by a broad "blue" band peaking ∼430 nm, which consists of at least three elementary bands that correspond to different host defects. Excitation of the host luminescence showed the broad band with a maximum at 360 nm. Characteristic bands of d–d transitions of Mn²⁺ ions and f–f transitions of Eu³⁺ ions together with charge-transfer bands (CTB) of these ions were also found on the excitation spectra. Mn²⁺ and Eu³⁺ co-doped samples emit in green and red spectral regions. Mn²⁺ ions are responsible for the green emission band at 505 nm (⁴T₁→⁶A₁ transition). The studies of photoluminescence spectra of activated samples with different Eu³⁺ ions content show characteristic f–f luminesecence of Eu³⁺ ions. The maximum of Eu³⁺ emission was found at 618 nm (⁵D₀→⁷F₂) and optimal concentration of activator ions was around 4 mol. %. - Highlights: • Host luminescence is presented by a broad band with a maximum at 430 nm and has a complex nature. • Charge transfer bands from lattice to Mn²⁺ and Eu³⁺ ions were found around 260 and 280 nm, respectively. • Activator luminescence intensity reaches the maximum at 4 mol.% of Eu³⁺ ions concentration.