Electrophysical and optical properties of InP after heavily neutron irradiation

Creators

  • 1. Tomskij Gosudarstvennyj Univ., Sibirskij Fiziko-Tekhnicheskij Inst. im. V.D. Kuznetsova, Tomsk (Russian Federation)
  • 2. Filial FGUP Nauchno-Issledovatel'skij Fiziko-Khimicheskij Inst. im. L.Ya. Karpova, Moscow (Russian Federation)

Description

Electrophysical properties and optical absorption spectra of InP irradiated with fast neutrons (E>0.1 MeV, D≤1019 cm-2) and reactor neutrons (D≤1x1019 cm-2), and the changing of these properties during the post-irradiation annealing up to 900 Deg C are presented. The results of the optical investigations reveal that free charge carriers are appeared in the heavily neutron-irradiated InP after annealing up to 500 Deg C only. The efficiency of the neutron transmutation doping and the quality of InP are estimated

Abstract (Russian)

Представлены результаты исследований эдектрофизических свойств и спектров оптического поглощения InP, облученного быстрыми нейтронами (E>0.1 МэВ, D≤1019 см-2) и полным спектром реакторных нейтронов (D≤1x1019 см-2), а также характер изменения этих свойств при последующей термообработке материала до 900 град C. Результаты оптических исследований свидетельствуют о том, что свободные носители заряда в сильно облученном нейтронами InP появляются только после отжига выше 500 град C. Оценена эффективность ядерного легирования и качество полученного InP

Additional details

Additional titles

Original title (Russian)
Электрофизические и оптические свойства InP, облученного большими интегральными потоками нейтронов

Publishing Information

Journal Title
Fizika i Tekhnika Poluprovodnikov
Journal Volume
39
Journal Issue
5
Journal Page Range
p. 528-534
ISSN
0015-3222
CODEN
FTPPA4

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
38029700
Subject category
S75: CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY;
Descriptors DEI
ANNEALING; DIAGRAMS; ELECTRON DENSITY; FAST NEUTRONS; FERMI LEVEL; HALL EFFECT; INDIUM PHOSPHIDES; KEV RANGE 100-1000; N-TYPE CONDUCTORS; NEUTRON FLUX; OPACITY; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K; THERMAL NEUTRONS; TRANSMUTATION
Descriptors DEC
BARYONS; ELEMENTARY PARTICLES; ENERGY LEVELS; ENERGY RANGE; FERMIONS; HADRONS; HEAT TREATMENTS; INDIUM COMPOUNDS; INFORMATION; KEV RANGE; MATERIALS; NEUTRONS; NUCLEONS; OPTICAL PROPERTIES; PHOSPHIDES; PHOSPHORUS COMPOUNDS; PHYSICAL PROPERTIES; PNICTIDES; RADIATION FLUX; SEMICONDUCTOR MATERIALS; TEMPERATURE RANGE

Optional Information

Notes
30 refs., 6 figs., 2 tabs.