The magnetic properties of powdered and compacted microcrystalline permalloy

The aim of this work is to investigate the magnetic properties of powdered and compacted microcrystalline Ni-Fe (81 wt% of Ni) permalloy. It was found by investigating the influence of mechanical milling on the magnetic properties of powder samples prepared by milling of the ribbon that the alloy remains a solid solution with stable structure during the whole milling process. With decreasing particle size the rotation of magnetization vector gradually becomes dominant magnetization process and thus coercivity increases. After compaction of the powder by uniaxial hot pressing the magnetic contact between powder particles is recreated and for resulting bulk the displacement of the domain walls becomes dominant magnetization process with coercivity of 11 A/m (comparable with the coercivity of conventional permalloy)