Cyclic Creep Behavior of Modified 9Cr-1Mo Steel at 600 .deg. C

Cyclic deformation behavior is important in practice because high-temperature structural components are exposed under the cyclic conditions of repeated loading. In static creep (SC), the response of the material is simple as a static state of monotonic loading. However, in cyclic creep (CC), it is complex as dynamic loading. Cyclic creep data have been rarely reported until now. In particular, it is not understood well whether cyclic creep will accelerate or retard the creep rate compared with static creep, because it is not only the plastic deformation under cyclic loading is drastically different from monotonic loading, but also the cyclic response is dependent on the cycling frequency, stress range, stress ratio, and hold periods of cycling. Therefore, it is necessary to clarify the cyclic creep behavior influencing the creep deformation and fracture process. In this study, a series of cyclic creep tests was carried out using magnitudes of stress range of constant stress ratio (R=0.1) under continuous tension-tension loading cycles at a hold time of 10 minutes. Cyclic curves were monitored and obtained with time variations, and the properties of the cyclic creep tests were compared with those of static creep tests. The fracture microstructures were observed and analyzed