Orientation relationship in Eurofer martensitic steels

Both TEM and SEM/EBSD orientation measurements are carried out on a Eurofer97 martensitic steel. The influence of the prior austenitic grain size is studied using dedicated heat treatments. The intra laths misorientation is estimated by TEM. SEM/EBSD orientation mapping enable to study the actual orientation relationship (OR) between the parent austenitic phase and the martensitic phase. Neither the Nishiyama-Wasserman nor the Kurdjumov-Sachs OR is able to account for both the misorientation angle distributions, the pole figure and the misorientation axes measured. The mixed OR recently proposed by Gourgues et al. (Electron backscattering diffraction study of acicular ferrite, bainite, and martensite steel microstructures, Mater. Sci. Tech. 16 (2000), p. 26-40.) and Sonderegger et al. (Martensite laths in creep resistant martensitic 9-12% Cr steels - Calculation and measurement of misorientations, Mater. Characterization (2006), in Press.) seems to be able to account for most of these results. Based on this OR, a new angular criterion is proposed to detect blocks of laths. (authors)