Long-term Creep Life Prediction for Type 316LN Stainless Steel

Since Sodium Fast Cooled Reactor (SFR) components are designed to be use for more than 30 years at a high temperature of 550 .deg. C, one of the most important properties of these components is the long term creep behavior. To accurately predict the long-term creep life of the components, it is essential to achieve reliable long-term test data beyond their design life. But, it is difficult to actually obtain long duration data because it is time-consuming work. So far, a variety of time-temperature parameters (TTPs) have been developed to predict a long-term creep life from shorter-time tests at higher temperatures. Among them, the Larson-Miller, the Orr-Sherby-Dorn, the Manson-Harferd and the Manson-Succop parameters have been typically used. None of these parameters has an overwhelming preference, and they have certain inherent restrictions imposed on their data in the application of the TTPs parameters. Meanwhile, it has been reported that the Minimum Commitment Method (MCM) proposed by Manson and Ensign has a greater flexibility for a creep rupture analysis. Thus, the MCM will be useful as another approach. Until now, the applicability of the MCM has not been investigated for type 316LN SS because of insufficient creep data. In this paper, the MCM was applied to predict a long-term creep life of type 316LN stainless steel (SS). Lots of creep rupture data was collected through literature surveys and the experimental data of KAERI. Using the short-term experimental data for under 2,000 hours, a longer-time rupture above 105 hours was predicted by the MCM at temperatures from 550 .deg. C to 800 .deg. C