Structure and superconducting properties of Nb3Pb compound
- 1. NYaTs RK, Inst. Yadernoj Fiziki, Almaty (Kazakhstan)
Description
From solid solutions of lead in niobium, produced by the method of codeposition of metal-bearing plasma jets on a mobile substrate, an intermetallic compound Nb3Pb is synthesized at a temperature of 1150 deg C within a concentration range from 11.1 to 22.7 at. % of lead, and its lattice parameter is determined over all range studied. It is established that the lattice parameter of Nb3Pb remains unchanged and is equal to 0.5952 nm as the intermetallic compound is synthesized from initial solid solutions. It is revealed that critical temperature of superconducting transition equals 5.6 K for a Nb3Pb film synthesized from solid solution with 20.9 at. % of lead, as this takes place, the value of critical current density is determined to be not less than 4 x 104 A cm-2
Abstract (Russian)
При температуре 1150 град С из пленок твердых растворов свинца в ниобии, полученных методом совместного соосаждения потоков металлсодержащей плазмы на подвижную подложку, в интервале концентраций от 11.1 до 22.7 ат. % свинца осуществлен синтез интерметаллического соединения Nb3Pb и определен параметр его решетки во всем исследованном интервале. Установлено, что параметр решетки Nb3Pb остается постоянным и равным 0.5952 нм при синтезе интерметаллида из исходных твердых растворов. Определено, что критическая температура перехода в сверхпроводящее состояние пленки Nb3Pb, синтезированной из твердого раствора с 20.9 ат. % свинца, составляет 5.6 К, при этом значение критической плотности тока определено не меньше, чем 4 x 104 A см-2Additional details
Additional titles
- Original title (Russian)
- Структура и сверхпроводящие свойства интерметаллида Нб
Publishing Information
- Journal Title
- Fizika Metallov i Metallovedenie
- Journal Volume
- 97
- Journal Issue
- 2
- Journal Page Range
- p. 21-23
- ISSN
- 0015-3230
- CODEN
- FMMEA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 36094678
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- FILMS; INTERMETALLIC COMPOUNDS; LATTICE PARAMETERS; LEAD ALLOYS; NIOBIUM ALLOYS; SOLID SOLUTIONS; SUPERCONDUCTIVITY; SUPERCONDUCTORS; SYNTHESIS; TEMPERATURE RANGE 0000-0013 K; TRANSITION TEMPERATURE; VAPOR DEPOSITED COATINGS
- Descriptors DEC
- ALLOYS; COATINGS; DISPERSIONS; ELECTRIC CONDUCTIVITY; ELECTRICAL PROPERTIES; HOMOGENEOUS MIXTURES; MIXTURES; PHYSICAL PROPERTIES; SOLUTIONS; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 6 refs., 2 figs.