Hard coatings based on ternary compounds

  • 1. RAN, Inst. Mikroehlektroniki i Informatiki, Yaroslavl' (Russian Federation)
  • 2. Metropoliten Univ., Manchester (United Kingdom)
  • 3. Moskovskij Gosudarstvennyj Univ. im. M.V. Lomonosova, Moscow (Russian Federation)

Description

Ion-assisted method of deposition was used for production of hard coatings (Ti1-xCrx)N compounds. Analysis of chemical and phase composition, structure and hardness of films, depending on condition of ion bombardment and deposition, was carried out. The possibility of production of the stoichiometric CrN hard coatings with hardness of 30 GPa was shown. For ternary (Ti1-xCrx)N compounds the dependence of film properties on the content of Cr and Ti was observed and explained. Maximum hardness, more than 30 GPa, for (TiCr2)N coatings has been obtained

Abstract (Russian)

Разработана методика упрочняющих покрытий на основе нитридов (Ti1-xCrx)N с применением ионного ассистирования. Проведен анализ химического и фазового состава пленок, их структуры и прочности для разных условий ионной бомбардировки и осаждения. Показана возможность изготовления плотных упрочняющих покрытий на основе CrN стехиометрического состава с микротвердостью, достигающей 30 ГПа. Для тройных соединений (Ti1-xCrx)N изучена и объяснена зависимость свойств покрытий от содержания в них Cr и Ti. Микротвердость более 30 ГПа получена для пленок (TiCr2)N

Additional details

Additional titles

Original title (Russian)
Uprochnyayushchie pokrytiya na osnove trojnykh soedinenij

Publishing Information

Journal Title
Poverkhnost'. Rentgenovskie, Sinkhrotronnye i Nejtronnye Issledovaniya
Journal Issue
no.4
Journal Page Range
p. 106-110
ISSN
1028-0960

Conference

Title
34.conference on physics of interaction of charged particles with crystals
Original Conference Title
XXXIV Mezhdunarodnaya konferentsiya po fizike vzaimodejstviya zaryazhennykh chastits s kristallami
Dates
31 May - 4 Jun 2004
Place
Moscow (Russian Federation)

Optional Information

Notes
28 refs., 5 figs., 2 tabs.