Vesicular delivery of crystalline calcium minerals to ECM in biomineralized nanoclay composites

The mechanisms of mineralization and new bone formation were explored in newly formed extracellular matrix in a nanoclay based composite. Nanoclay films were prepared by intercalating the clays with amino acids and using the amino acids for mineralization of hydroxyapatite. The biomineralized hydroxyapatite (HAP) inside nanoclay galleries or in situ HAP/clay was further used to make films (substrates) using polycaprolactone (PCL) that were seeded with mesenchymal stem cells in a two-stage seeding process. SEM imaging experiments performed on PCL/in situ HAPclay composite films seeded with human MSCs indicated formation of matrix vesicles. The vesicles appear to emerge from the cells that are adhered to the nanoclay HAP films and also deposited in the extracellular space. Vesicles are also observed to be embedded in the cells or under the surface of cells. Crystalline structures with Ca and P were found inside vesicles. The Ca/P ratios obtained using energy dispersive spectroscopy indicate values ranging from below 0.7 to the stoichiometric HAP value of 1.67. The Ca/P ratios were obtained to be closer to the stoichiometric value for single seeding experiments as compared to the double seeding experiments indicating more new bone formation in double seeding experiments. New bone formation with bone mimetic mineralization is thus observed on the in situ HAP nanoclay PCL samples. Hence the PCL/in situ HAPclay composites besides being osteoinductive are also capable of providing a favorable micro-environment for cell dependent processes involved in bone mineral formation. (paper)