Secondary recrystallization behavior in a twin-roll cast grain-oriented electrical steel

The microstructure and texture evolution along the processing was investigated with a particular focus on the secondary recrystallization behavior in a 0.23 mm-thick twin-roll cast grain-oriented electrical steel. A striking feature is that Goss orientation originated during twin-roll casting as a result of shear deformation and it was further enhanced during hot rolling and normalizing. After primary recrystallization annealing, a homogeneous microstructure associated with a sharp γ-fiber texture was produced. During secondary recrystallization annealing, the γ-fiber texture was first strengthened and weakened with increasing temperature prior to the onset of secondary recrystallization. Goss grains always exhibited more 20–45° misoriented boundaries than the matrix. The matrix was quite stable during secondary recrystallization with the aid of dense inhibitors. Finally, a complete secondary recrystallization microstructure consisting of large Goss grains was produced. The grain boundary characteristics distribution indicated that the high energy model was responsible for the abnormal growth of Goss grains under the present conditions. - Highlights: • A 0.23 mm twin-roll cast grain-oriented silicon steel sheet was produced. • Goss orientation originated during twin-roll casting. • Secondary recrystallization behavior was briefly investigated. • γ-fiber texture was enhanced prior to the onset of secondary recrystallization. • A complete secondary recrystallization microstructure was produced.