Tensile and Charpy impact properties of an ODS ferritic/martensitic steel 9Cr–1.8W–0.5Ti–0.35Y2O3

Highlights: • The tensile property and Charpy impact were tested. • Both strength and plasticity in LT direction are better than that of TL direction. • The LSE was more than 65% of the USE from absorbed energy curve. • The initiation and propagation energy at different temperatures were calculated. • High LSE and dimples on the fracture surface indicated good toughness at −60 °C. - Abstract: A 9Cr-ODS ferritic/martensitic steel with a composition of 9Cr–1.8W–0.5Ti–0.35Y2O3 was fabricated by mechanical alloying and hot isostatic pressing, followed by hot rolling. Tensile properties were measured at room temperature (23 °C) and 700 °C in the rolling direction (LT) and the transverse direction (TL). The ultimate tensile strength (UTS) of the as-rolled samples in both directions reached 990 MPa at 23 °C, and still maintained at 260 MPa at 700 °C. The tensile strength and elongation of the rolling direction was greater than that of the transverse direction. The Charpy impact was tested from −100 to 100 °C in the LT direction. The lower shelf energy (LSE) was more than 65% of the upper shelf energy (USE). The total absorbed energy was separated into the energies for crack initiation and propagation. The propagation energy was always higher than the initiation energy in the range of temperatures tested. The ductile-to-brittle transition temperature (DBTT) of the rolled 9Cr ODS evaluated by an absorbed energy curve was about 0 °C. However, the high LSE and the fracture surface that still contained dimples at lower shelf indicated good toughness of the as-rolled 9Cr ODS steels at temperature of −60 °C