Kinetics of Transformation of Al₂O₃ to MgO·Al₂O₃ Spinel Inclusions in Mg-Containing Steel

During ladle furnace refining, initial Al₂O₃ inclusions generally transform into MgO·Al₂O₃ spinel inclusions; these generated spinel inclusions consequently deteriorate the product quality. In this study, the transformation from Al₂O₃ to MgO·Al₂O₃ was investigated by immersing an Al₂O₃ rod into molten steel, which was in equilibrium with both MgO and MgO·Al₂O₃ spinel-saturated slag. A spinel layer, with a thickness of 4 μm, was generated on the Al₂O₃ rod surface just 10 s after its immersion at 1873 K (1600 °C). The thickness of the formed spinel layer increased with the immersion period and temperature. Moreover, the MgO content of the generated spinel layer also increased with the immersion period. In this study, the chemical reaction rate at 1873 K (1600 °C) was assumed to be sufficiently high, and only diffusion was considered as a rate-controlling step for this transformation. By evaluating the activation energy, MgO diffusion in the generated spinel layer was found to be the rate-controlling step. In addition, this estimation was confirmed by observing the Mg and Al concentration gradients in the generated spinel layer. The results of this study suggest that the MgO diffusion in the spinel inclusions plays a substantial role with regard to their formation kinetics.