Investigation of Ductile-to-Brittle Transition of RPV Materials by using the Pre-cracked Charpy Impact Data

Much recent work in the field of elastic-plastic fracture mechanics has been directed to developing a mechanics-based relationship between the onset of cleavage fracture in structural components and that of Charpy V-notch specimens. The assessing processes of the cracks located in the reactor pressure vessel (RPV) is described in the ASME code Sec. III, App. G and Sec. XI, App. A. The RTNDT obtained from the impact test using standard Charpy V-notch (CVN) specimens is used as a reference temperature to assess the integrity of RPV materials. The initial RTNDT, for the Linde 80 weld, was determined by the 67.8J Charpy impact energy instead of drop weight test. Generally, Linde 80 weld has low upper-shelf energy. The initial RTNDT obtained from the Charpy impact energy curve has been considered overly conservative. Recently, master curve method has been investigated to assess the integrity of RPV materials directly. The initial RTT0 obtained from the master curve method is considered more realistic than the initial RTNDT obtained from impact test for low upper-shelf fracture toughness RPV materials. In this research, the correlation of transition regions between the master curves and the Charpy impact energy curves was investigated using the dynamic fracture toughness curve and the impact energy curve obtained from the impact test of pre-cracked Charpy (PCC) specimens. For the low toughness RPV material the ductile-to-brittle transition corresponding to the static master curve was anticipated using the invested correlation