Dissolution of carbon-containing particles such as soot, cementite, and VC carbides in FCC Fe-Ni alloys upon severe cold deformation
- 1. Inst. Fiziki Metallov UrO RAN, Ekaterinburg (Russian Federation)
Description
The possibility of dynamic dissolution of carbon and carbon-containing particles in N36 and 90N29G4F3 FCC alloys is studied. Powder mixtures of the alloys, carbon black, cementite or VC0.86 carbide are subjected to severe cold deformation by shear within the reduction ratio range from 6.2 to 8.3. The following regularities of solid solution formation are revealed: 1) a carbon concentration in the alloy obtained is dependent on the type of initial carbon-containing component and decreases in a succession of carbon black → Fe3C → VC; 2) the initiation of dissolution is preceded by an incubation period, probably associated with the decomposition of carbon-containing particles and the capture of carbon by edge dislocations; 3) the synthesis of a Fe-Ni-C solid solution in an alloy H36 - carbon, black powder mixture starts at lower deformation degree than in the case of Fe3C and VC
Abstract (Russian)
Исследована возможность динамического растворения углерода и карбидных частиц в ГЦК-сплавах Н36 и 90Н29Г4Ф3. Смеси порошков сплавов и сажи, цементита или карбида VC0.86 подвергали интенсивной холодной деформации сдвигом со степенями деформации от 6,2 до 8,3. Установлены следующие закономерности формирования твердого раствора: 1) концентрация углерода в сплаве зависит от типа исходной углеродсодержащей компоненты и уменьшается в ряду сажа → Fe3C → VC; 2) началу растворения предшествует инкубационный период, связанный, вероятно, с распадом углеродсодержащих частиц и захватом углерода краевыми дислокациями; 3) синтез твердого раствора Fe-Ni-C порошковой смеси сплава Н36 с сажей начинается при меньших степенях деформации, чем в случаях с Fe3C и VCAdditional details
Additional titles
- Original title (Russian)
- Растворение углеродсодержащих частиц - сажи, цемента и карбидов VC в GTsK-сплавах Фе-Ни при сильной холодной деформации
Publishing Information
- Journal Title
- Fizika Metallov i Metallovedenie
- Journal Volume
- 91
- Journal Issue
- 3
- Journal Page Range
- p. 88-96
- ISSN
- 0015-3230
- CODEN
- FMMEA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 33016028
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CARBON BLACK; CEMENTITE; COLD WORKING; DISSOLUTION; FCC LATTICES; IRON BASE ALLOYS; NICKEL ALLOYS; POWDERS; SOLID SOLUTIONS; STRAINS; VANADIUM CARBIDES
- Descriptors DEC
- ALLOYS; CARBIDES; CARBON; CARBON COMPOUNDS; CRYSTAL LATTICES; CRYSTAL STRUCTURE; CUBIC LATTICES; DISPERSIONS; ELEMENTS; FABRICATION; HOMOGENEOUS MIXTURES; INTERMETALLIC COMPOUNDS; IRON ALLOYS; IRON CARBIDES; IRON COMPOUNDS; MATERIALS WORKING; MIXTURES; NONMETALS; SOLUTIONS; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENT COMPOUNDS; VANADIUM COMPOUNDS
Optional Information
- Notes
- 30 refs.; 8 figs.