A facile in situ solvothermal method for two-dimensional layered g-C₃N₄/SnS₂ p-n heterojunction composites with efficient visible-light photocatalytic activity

To overcome the fast recombination rate of electron-hole pairs of individual SnS₂, p-n heterojunction g-C₃N₄/SnS₂ composites were fabricated as high-efficiency visible-light photocatalyst to photodegradate the organic dye MB. The morphologies, structures, compositions, and photocatalytic properties were characterized. The SnS₂ shows two-dimensional layer structure with an average thickness of 20 nm and diameter size of about 2 μm, and the g-C₃N₄ nanoflakes were uniformly deposited on the surface of SnS₂ nanosheets. In comparison with the bare g-C₃N₄ and SnS₂, the composites show improved photocatalytic activity under visible light, which is sensitive to the content of g-C₃N₄. In particular, the 15% g-C₃N₄/SnS₂ composites exhibit the highest photocatalytic activity and outstanding reusability, which can degrade 88.01% MB after only 1 h in the visible light (#lambda# > 420 nm) range. The g-C₃N₄/SnS₂ heterojunction composites show outstanding reusability after four times cycling experiments. The improved photocatalytic activities of composites are attributed to abundant active species, increased charge separation, and decreased electron-hole pair recombination, which originated from the large specific surface area and efficient interfacial transport of photo-induced charge carriers between SnS₂ and g-C₃N₄. These results suggest that the two-dimensional layered g-C₃N₄/SnS₂ p-n heterojunction composites are promised to be a high-efficiency visible-light photocatalyst.