Synthesis of hierarchical MoS₂ microspheres composed of nanosheets assembled via facile hydrothermal method as anode material for lithium-ion batteries

A hierarchical MoS₂ architecture composed of nanosheet-assembled microspheres with an expanded interplanar spacing of the (002) planes was successfully prepared via a simple hydrothermal reaction. Electron microscopy studies revealed formation of the MoS₂ microspheres with an average diameter of 230 nm. It was shown that the hierarchical structure of MoS₂ microspheres possesses both the merits of nanometer-sized building blocks and micrometer-sized assemblies, which offer high surface area for fast kinetics and buffers the volume expansion during lithium insertion/deinsertion, respectively. The micrometer-sized assemblies were found to contribute to the enhanced electrochemical stabilities of the electrode materials. The mentioned advantages of the MoS₂ electrode prepared in this work allowed enhanced cyclability and high rate capability of the material. Along with this, the material delivered a high initial discharge capacity of 1206 mAh g⁻¹ and a reversible discharge capacity of 653 mAh g⁻¹ after 100 cycles at a current density of 100 mA g⁻¹. Furthermore, the material delivered a high reversible capacity of 480 mAh g⁻¹ at a high current density of 1000 mA g⁻¹.