EB radiation crosslinking of elastomers

Complete text of publication follows. The first paper in the series described by the general title, starts with radiation crosslinking of hydrogenated butadiene-nitrile rubber (HBNR). This high-tech elastomer is obtained by catalytic hydrogenation of >C=C< double bonds in butadiene-nitrile rubber (NBR) without affecting the nitrile groups. Radiation induced crosslinking is proposed as alternative to chemical methods of crosslinking. Two kinds of commercial products were chosen of 43% of nitrile and the degree of hydrogenation resp. >99.5 and 94.5% of starting double bonds. Samples were irradiated with 10 MeV electrons, monoenergetical, 6 kW power, used as scanned beam over the conveyor, securing homogeneity of dose distribution. The doses were up to 300 kGy, applied in 20 kGy increments to avoid radiation generated heating of the material. The influence of presence or absence of oxygen was considered. Irradiated samples were investigated for the extend of crosslinking in the function of dose and for properties important for understanding of mechanisms. Samples are transparent, what allowed conventional absorption spectrophotometry, also time resolved. The quantitative interpretation of results shows that for 100 crosslinks there are 6-9 acts of chain-scission. It is less, than expected from the participation of multi-ionization spurs, also in the solid state, as announced during the previous, 9th Tihany Conference. However, the apparent lower yield of multi-ionization spurs is explained by partial conversion of products into crosslinks of specific type. Our investigations confirm the usefulness of consideration of radiation spurs in polymers as well as in all, low LET irradiated media