Characterization of laboratory and industrial CrN/CrCN/diamond-like carbon coatings

This work reports on laboratorial and experimental wear behaviour studies about a multi-layered film deposited by PVD (Physical Vapour Deposition) unbalanced magnetron sputtering. The film consists of three different layers: CrN in the bottom, CrCN as intermediate layer and DLC (diamond-like carbon) on the top. Film characterization was done using techniques such as Scanning Electron Microscopy, Energy Dispersive X-ray Spectroscopy, Atomic Force Microscopy and X-ray diffraction. Scratch-tests, nanoindentation analysis and ball-cratering wear tests were used in order to measure the adhesion critical load, hardness and wear coefficient, respectively. Experimental tests were developed letting one to realise the suitability of this film for mould cavities used on injection moulding machines that produce automotive parts in polypropylene reinforced with 30% (wt.) glass fibres, because this composite material performs severe abrasion on injection moulding which brings important challenges to surface wear resistance. Experimental tests revealed that, after 135,000 injection cycles, multi-layer coating improved significantly the performance previously revealed by uncoated samples. The good results achieved by this film can be partially assigned to DLC top layer due to its low friction coefficient. This paper discusses these results, comparing them with some other PVD coatings already tested in the same conditions. - Highlights: • This coating presents a very good adhesion to the P20 steel substrate. • Surface wear performance is largely improved by the use of this coating. • Coating wear resistance is about 58.2 times higher than the uncoated substrate. • This film presents high suitability for application in mould cavities