Physical Properties of indium doped Cadmium sulfide thin films prepared by (SPT)

Various thin films of cadmium sulfide doped with different weight ratios (wt %) of indium (CdS: In), were prepared on glass substrates by Spray pyrolysis technique (SPT), The Microstructural, topography and optical characteristics were studied. Pure films and doped with In 1%. The results obtained revealed that the growth toward single crystalline hexagonal- cubic phases. The dominant reflection is in the direction (101) plane with a crystalline size 47.55 nm, which is calculated utilizing Scherrer equation. The increase in In to 3% tends the structure to be the poly crystalline with the existence of the prevalent reflection in the direction of (101) plane with a the crystal size of 53.89 nm. The topography measurements showed that the surfaces of the nanostructured are in the form of rods with a height of 1.99 nm and a diameter of 50-60 nm. The rod height decreased with the increasing in doping weight ratios, while the diameter of the rod increased. The optical measurements showed lower transmittance with the increasing of doping from T% 95 to T% 64. A decrease in the optical energy gap value was noticed. (paper)