The deviatoric response of three dense glasses under shock loading conditions

In-material longitudinal and lateral stress histories in three dense, silica-based glasses were directly measured by embedded manganin stress gauges during plate impact experiments. Lateral stress profiles in all of the materials show evidence of failure fronts that behave in a similar manner to those observed in open-structured glasses. The measured stress histories were used to calculate the deviatoric responses and results indicate that ahead of the failure front the shear stress increases linearly along the estimated elastic response. Behind the failure front, however, the shear stress appears to first decrease and then increase as the pressure increases, contrary to a previous interpretation