Evaluation of mechanical properties and microstructural characterization of consolidated Cobalt-Chromium-Molybdenum obtained by selective laser melting and precision casting

The objective of this work was to study the mechanical properties and microstructural characterization of specimens of the Co-Cr-Mo alloy obtained by additive manufacturing -selective laser melting (SLM) and precision casting aiming at the manufacture of dental prostheses. The following steps were carried out on Co-Cr-Mo gas-atomized powders: 1) investigation of the physical, chemical and thermal properties of atomized powders in different grain sizes (denominated: D1 <15 μm, D2 20-50 μm and D3 > 75 μm); 2) the consolidation of standard specimens via consolidation techniques; 3) characterization of consolidated by analysis of: cytotoxicity, porosity, X ray diffraction and dilatometry; 4) mechanical characterization of tensile, 3 point bending, hardness (macro and micro Vickers) tests and microstructural characterization (optical and scanning electron microscopy). In general, the results observed were: the grain size D2 (20-50 μm) is the one that best fits in the analysis of packaging, for the consolidation by SLM; the biocompatibility of the samples obtained a positive result for both processing techniques; the mechanical evaluation of the specimens shows that the SLM technique provides superior mechanical properties (yield stress, rupture stress, maximum stress, elongation and hardness), compared to those obtained by the precision casting technique; the microstructure obtained by the SLM process results in an ultrafine grains with high chemical homogeneity, differentiated by the gross dendritic microstructure in the casting process. In this way, the development of the present study evidenced superior quality in manufacturing customized dental components (copings) by SLM technique compared to precision casting. (author)