Investigations on the influence of sodium on the creep rupture and creep behaviour of the steel X5 CrNi 18 9 (AISI 304, W.-No. 1.4301) at 823 K

Creators

Description

We did not observe any effects of sodium on the time to rupture, the time to reach limited strain and the creep rate of steel X5 CrNi 18 9 (AISI 304, W.-No. 1.4301) in creep rupture tests at 823 K in flowing sodium up to 2000 hours exposure time. Only the fracture mode is influenced by the liquid sodium. Sodium causes intercrystalline precracking, the ultimate strain values are somewhat reduced. Exchange of carbon or nitrogen did not occur to such an extent that it could affect the mechanical properties. (orig.)

Abstract (German)

In den Zeitstand- und Kriechversuchen an dem Stahl X5 CrNi 18 9 (1.4301, AISI 304) bei 823 K in stroemendem Natrium wurde bis zu Auslagerungszeiten von ueber 2000 Stunden kein Effekt auf die Standzeit, die Zeitdehngrenzen und die Kriechgeschwindigkeit beobachtet. Lediglich das Bruchverhalten des Stahls wird durch Natrium veraendert. Natrium verursacht interkristallinen Anbruch, die Bruchdehnung wird dadurch verringert. Kohlenstoff oder Stickstoff wurden dabei nicht mit dem Natrium in einem Masse ausgetauscht, dass Auswirkungen auf die mechanischen Eigenschaften eintreten konnten. (orig.)

Additional details

Additional titles

Original title (German)
Untersuchungen zum Natriumeinfluss auf das Zeitstand- und Kriechverhalten des Stahls X5 CrNi 18 9 (AISI 304, W.-Nr. 1.4301) bei 823 K

Publishing Information

Journal Title
Z. Werkstofftech.
Journal Volume
12
Journal Issue
7
Series
Z. Werkstofftech.
Journal Page Range
250-256
ISSN
0049-8688

INIS

Country of Publication
Germany
Country of Input or Organization
Germany
INIS RN
13653149
Subject category
S36: MATERIALS SCIENCE; S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY;
Descriptors DEI
CARBON; CORROSION; CREEP; ELONGATION; FRACTURE PROPERTIES; HIGH TEMPERATURE; LIQUID METALS; MICROSTRUCTURE; NITROGEN; RUPTURES; SODIUM; STAINLESS STEEL-304; STEEL-DIN-1-4301; STRAINS; TIME DEPENDENCE
Descriptors DEC
ALKALI METALS; ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CHEMICAL REACTIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; CRYSTAL STRUCTURE; DEFORMATION; ELEMENTS; FAILURES; FLUIDS; HEAT RESISTING ALLOYS; IRON ALLOYS; IRON BASE ALLOYS; LIQUIDS; MANGANESE ALLOYS; MECHANICAL PROPERTIES; METALS; NICKEL ALLOYS; NONMETALS; SILICON ADDITIONS; STAINLESS STEELS; STEELS; TRANSITION ELEMENT ALLOYS