Honeycomb-like graphitic ordered macroporous carbon prepared by pyrolysis of ammonium bicarbonate

Graphical abstract: Honeycomb-like graphitic macroporous carbon (HGMC) with big pores centered at 1-3 μm, has been prepared by controlling the reaction temperature and amount of NH4HCO3 at 550 oC in a sealed reaction system. Possible formation processes of HGMC are discussed on the experimental results. It is believed that the in situ formed MgO microparticles play a template role during the preparation of HGMC. Highlights: → Honeycomb-like graphitic carbon was synthesized at 550 oC. → The honeycomb-like graphitic carbon is macroposous structures. → The formed MgO microparticles play a template role during the HGMC formation. → The method can be expended to synthesize other porous or hollow carbon material. -- Abstract: Honeycomb-like graphitic macroporous carbon (HGMC) was synthesized by means of pyrolysis of NH4HCO3 using Mg powder as reductant in an autoclave at 550 oC. The characterization of structure and morphology was carried out by X-ray diffraction (XRD), Raman spectrum, field-emission scanning electron microscopy (FESEM), and (High-resolution) transmission electron microscope [(HR)TEM]. The results of nitrogen adsorption-desorption indicate that the products are macropore materials with the pore size of 1-3 μm, and the Brunauer-Emett-Teller (BET) surface area was 14 m2/g. As a typical morphology, the possible growth process of HGMC was also investigated and discussed. The experimental results show that the in situ formed MgO microparticles play a template role during the HGMC formation.