Glass formation in the GeS2-EuS system
- 1. Inst. Obshchej i Neorganicheskoj Khimii im. V.I. Vernadskogo Natsional'noj Akademii Nauk Ukrainy, Kiev (Ukraine)
Description
Methods of differential thermal, X-ray diffraction and chemical analyses as well as IR-spectroscopy are applied to study crystalline and glass-like alloys of one of the most high-temperature glass-forming system of GeS2-EuS. Temperature conditions of vitrification, crystallization and melting in the system are refined. It is established that the temperature of vitrification decreases from 492 down to 448 Deg C with an europium monosulfide concentration increase. The most homogeneous glasses can be obtained at EuS contents up to 15 mol. %. To obtain homogeneous glasses with 25-30 mol. % EuS their cooling rate should be risen up to 20-30 Deg C/s
Abstract (Russian)
Методами дифференциального термического, рентгенофазового и химического анализов, а также ИК-спектроскопии исследованы кристаллические и стеклообразные сплавы одной из наиболее высокотемпературных стеклообразующих систем GeS2-EuS. Уточнены температурные условия стеклообразования, кристаллизации и плавления в данной системе. Установлено, что температура стеклования с увеличением концентрации моносульфида европия понижается с 492 до 448 град С. Наиболее однородные стекла можно получить при концентрациях EuS до 15 мол. %. Для получения однородных стекол, содержащих 25-30 мол. % EuS, требуется увеличение скорости их охлаждения до 20-30 град С/сAdditional details
Additional titles
- Original title (Russian)
- Стеклообразование в системе GeS
Publishing Information
- Journal Title
- Neorganicheskie Materialy
- Journal Volume
- 40
- Journal Issue
- 5
- Journal Page Range
- p. 628-632
- ISSN
- 0002-337X
- CODEN
- NEOMB8
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 36094720
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CONCENTRATION RATIO; CRYSTALLIZATION; DIFFERENTIAL THERMAL ANALYSIS; EUROPIUM SULFIDES; GERMANIUM SULFIDES; GLASS; INFRARED SPECTRA; MELTING; QUANTITATIVE CHEMICAL ANALYSIS; SYNTHESIS; TEMPERATURE RANGE 0400-1000 K; VITRIFICATION; X-RAY DIFFRACTION
- Descriptors DEC
- CHALCOGENIDES; CHEMICAL ANALYSIS; COHERENT SCATTERING; DIFFRACTION; EUROPIUM COMPOUNDS; GERMANIUM COMPOUNDS; PHASE TRANSFORMATIONS; RARE EARTH COMPOUNDS; SCATTERING; SPECTRA; SULFIDES; SULFUR COMPOUNDS; TEMPERATURE RANGE; THERMAL ANALYSIS
Optional Information
- Notes
- 15 refs., 5 figs.