Evaluation and comparison of non destructive testing (NDT)-results from the full-scale vessel and from other test specimens of nuclear power plant (NPP)-components. Pt. 2. Full-scale vessel. Final report
Description
The project was aimed at comparising the performance of various NDT-techniques which are used for the testing of NPP-components. Three institutions took part in this test. Partly they applied more than one technique. The evaluation of the test results was based on German standards (KTA), and for the participants from East Germany on Russian standards. The test specimen was the full-scale vessel at MPA, Stuttgart, which consists of parts of a BWR (AEG, steel 1.6751, A 508 Cl 2, 22 NiMoCr 3 7) and of parts of a PWR (KWU Steel 1.6310, 20 MnMoNi 55, A 533 B Cl). The identified flaw extensions were used as a measure for the quality of test results. The test results from the full-scale vessel confirmed the findings of part 1. The modern automated NDT-techniques showed good and partly very good efficiency. This especially holds for cladded and thick walled parts of the vessel. (orig.)
Availability note (English)
Available from TIB Hannover: F95B622+a.Abstract (German)
Zielstellung des Forschungsvorhabens ist ein Vergleich der unterschiedlichen Pruefverfahren hinsichtlich ihrer Leistungsfaehigkeit bei der Pruefung von Kernkraftwerkskomponenten. Beteiligt waren 3 Institutionen, z.T. wurden von diesen mehrere Pruefverfahren am Grossbehaelter eingesetzt. Die vorwiegend computergestuetzten bildgebenden Verfahren basierten auf dem deutschen (KTA) bzw. auf dem osteuropaeischen Regelwerk. Am Grossbehaelter der MPA Stuttgart, einem SWR-Druckbehaelter (AEG, Werkstoff 1.6751, 22 NiMoCr 3 7, A 508 Cl 2) ergaenzt durch Teile eines DWR (KWU Werkstoff 1.6310, 20 MnMoNi 55, A 533 B Cl), wurden zerstoerungsfreie Pruefungen durchgefuehrt. Zielstellung war der Vergleich der eingesetzten Pruefverfahren besonders bei der Beschreibung von Schweissnahtfehlern bzw. kuenstlichen Reflektoren in der Art von Schweissnahtfehlern. Als formloses Mass fuer die Einschaetzung der Guete der Pruefergebnisse wurden die ermittelten Ausdehnungen in den Koordinaten des Bezugssystems genutzt. Die Pruefergebnisse am Grossbehaelter bestaetigen die im 1. Teil getroffenen Aussagen dahingehend, dass die modernen automatisierten Prueftechniken gute, z.T. sehr gute Ergebnisse bei der Fehlerbeschreibung zeigen. Im Fall des Grossbehaelters bezieht sich diese Aussage besonders auf dickwandige plattierte Pruefobjekte. (orig.)Additional details
Additional titles
- Original title (German)
- Bewertung und Vergleich von Pruefergebnissen durch Werkstoff- und Schweissnahtuntersuchungen am Grossbehaelter Stuttgart und anderen praxisrelevanten Testkoerpern von KKW-Komponenten. T. 2. Grossbehaehlter. Abschlussbericht
Publishing Information
- Imprint Pagination
- 78 p.
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 26053049
- Subject category
- S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS; S42: ENGINEERING; S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS;
- Resource subtype / Literary indicator
- Non-conventional Literature
- Descriptors DEI
- AUTOMATION; BWR TYPE REACTORS; COMPARATIVE EVALUATIONS; DEFECTS; EFFICIENCY; IN-SERVICE INSPECTION; NONDESTRUCTIVE TESTING; ON-LINE MEASUREMENT SYSTEMS; PRESSURE VESSELS; PWR TYPE REACTORS; STEEL-NIMOCR; WELDED JOINTS
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ADDITIONS; CONTAINERS; ENRICHED URANIUM REACTORS; EVALUATION; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; INSPECTION; IRON ALLOYS; IRON BASE ALLOYS; JOINTS; LOW ALLOY STEELS; MATERIALS; MATERIALS TESTING; MOLYBDENUM ADDITIONS; NICKEL ADDITIONS; ON-LINE SYSTEMS; POWER REACTORS; REACTORS; STEELS; TESTING; THERMAL REACTORS; WATER COOLED REACTORS; WATER MODERATED REACTORS
Optional Information
- Contract/Grant/Project number
- Foerderkennzeichen BMFT 1500896
- Funding organization
- Bundesministerium fuer Forschung und Technologie, Bonn (Germany).