Water radiolysis in a crack tip under gamma ray irradiation

Under a non-irradiation condition, oxidant, e.g., O2 and H2O2, in a crack tip is supplied from the bulk water. But under irradiation conditions, even if the diffusion of radiolytic species is not sufficient, direct radiolysis in the crack tip causes high concentrations of radiolytic species. As a result of measurements and Monte Carlo calculation of gamma ray energy deposition, it has been confirmed that the energy deposition rate in the gap water is larger than that in the bulk water. The energy absorption rate increases as the gap width decreases and reaches 1.3 times that in the bulk water. In order to evaluate crack propagation rate for irradiation assisted stress corrosion cracking (IASCC) of stainless steel, a water radiolysis model in a crevice is proposed. A larger energy deposition rate in the crevice water produces many more radiolytic species, which causes high oxidant concentrations in spite of enhanced recombination of the species at the crevice inner surface. So, for IASCC evaluation, crevice water chemistry plays an important role to determine the crack propagation rate under irradiation. (authors)