Fracture toughness shifts in high-copper weldments (series 5 and 6)

The specific activities to be performed in this task are the: (1) continuation of Phase 2 of the Fifth Irradiation Series, and (2) completion of the Sixth Irradiation Series, including testing nine irradiated Italian crack-arrest specimens. The test results of the Italian crack-arrest specimens are being analyzed, and full details will be published in a NUREG report currently in preparation. The crack-mouth opening displacement (CMOD) was measured at a distance greater than that prescribed in the American Society for Testing and Materials (ASTM) open-quotes Test for Determining Plane-Strain Crack-Arrest Fracture Toughness, Kla, of Ferritic Steelsclose quotes (E 1221-88). A method for adjusting the CMOD to account for this has been developed and is presented. The correction was ∼4% for small specimens and ∼2% for the larger ones. As part of this task, irradiation of HSSI weld 73W to a high fluence [5 x 1019 neutrons/cm2 ( > 1 MeV)] will be performed to determine whether the KJc curve shape change observed in the Fifth HSSI Series is exacerbated. The design and fabrication of the temperature and dosimetry verification capsules are performed under this task, but for purposes of continuity, their progress will be reported under Task 6, where the design of the new irradiation facilities and capsules is performed