Effect of gamma irradiation on linear low density polyethylene/magnesium hydroxide/sepiolite composite

Radiation crosslinking is generally used to improve the thermo-mechanical properties of the composites. A study has been carried out to investigate the effect of gamma radiation on the thermo-mechanical properties of linear low density polyethylene containing magnesium hydroxide (MH) and sepiolite (SP) as non-halogenated flame retardant additives. The developed composites are irradiated at different doses upto maximum of 150 kGy. Infrared spectra of the irradiated composites reveal the reduction in the intensity of O-H band with increase in the absorbed doses, thus indicates a distinct structural change in MH at higher doses. The thermogravimetric analysis results of unirradiated and composites irradiated at low doses (≤75 kGy) show two steps weight loss, which is changed to single step at higher doses with lower thermal stability. The melting temperature (Tm) and crystallization temperature (Tc) of irradiated composites are lowered with irradiation whereas Vicat softening temperature (VST) is increased. The increasing trend in gel content with increase in the absorbed dose confirms the presence of crosslinked network. The mechanical properties, results show significant improvement in the modulus of irradiated composites. The results also confirm that MH gradually loses its OH functionality with irradiation. - Highlights: → We have studied the effect of γ radiation on LLDPE containing Mg(OH)2 and sepiolite. → IR spectra of the irradiated composites show reduction in the intensity of O-H band. → Reduction in OH band show a distinct structural change in Mg(OH)2 at higher doses. → TGA results show two steps weight loss at low doses and one step at higher doses. → These results confirm that MH gradually loses its OH functionality with irradiation.