Stress corrosion of austenitic steels in a sodium-soda medium
Description
Stress corrosion was studied on the materials (alloy 800, 316 and 316 L, stainless steels, etc...) used for fast breeder reactor secondary loops containing soda-contaminated sodium at 4000C to 5500C. Under particularly severe conditions (exposure for 1000 hours at up to 10 % soda content) an intergranular stress corrosion cracking process was observed above a temperature-dependent stress threshold. (author)
Additional details
Publishing Information
- Publisher
- British Nuclear Energy Society.
- Imprint Place
- London (UK)
- ISBN
- 0 7277 0209 2
- Imprint Title
- Liquid metal engineering and technology. 3 v. Proceedings of the 3. international conference held in Oxford on 9-13 April 1984
- Imprint Pagination
- 1516 p.
- Journal Page Range
- v. 2 p. 483-487.
Conference
- Title
- 3. international conference on liquid metal engineering and technology.
- Dates
- 9-13 Apr 1984.
- Place
- Oxford (UK).
INIS
- Country of Publication
- United Kingdom
- Country of Input or Organization
- United Kingdom
- INIS RN
- 17031279
- Subject category
- S36: MATERIALS SCIENCE; S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS;
- Resource subtype / Literary indicator
- Conference
- Descriptors DEI
- CRACK PROPAGATION; HIGH TEMPERATURE; INTERGRANULAR CORROSION; LMFBR TYPE REACTORS; SECONDARY COOLANT CIRCUITS; SODIUM; SODIUM OXIDES; STEEL-CR17NI12MO3; STEEL-CR17NI12MO3-L; STRESS CORROSION; TEMPERATURE DEPENDENCE
- Descriptors DEC
- ALKALI METAL COMPOUNDS; ALKALI METALS; ALLOYS; AUSTENITIC STEELS; BREEDER REACTORS; CARBON ADDITIONS; CHALCOGENIDES; CHEMICAL REACTIONS; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; CHROMIUM-NICKEL-MOLYBDENUM STE; COOLING SYSTEMS; CORROSION; CORROSION RESISTANT ALLOYS; ELEMENTS; EPITHERMAL REACTORS; FAST REACTORS; FBR TYPE REACTORS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; LIQUID METAL COOLED REACTORS; LOW CARBON-HIGH ALLOY STEELS; METALS; MOLYBDENUM ALLOYS; NICKEL ALLOYS; OXIDES; OXYGEN COMPOUNDS; REACTOR COMPONENTS; REACTOR COOLING SYSTEMS; REACTORS; SODIUM COMPOUNDS; STAINLESS STEELS; STEELS