Large stable crack growth in fracture mechanics specimen
Creators
- 1. Fraunhofer-Inst. fuer Werkstoffmechanik, Freiburg (Germany)
- 2. Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin (Germany)
Description
This is a report on the crack resistance behaviour of the STE 460 steel on CT 25 and CCT 25 samples with side notches according to the J concept, from the J-controlled area to a crack growth of about 8 mm. Numerical simulation of the ductile crack growth controlled by JR curves for EVZ models of the sample geometries make an analysis possible of how well the standards, guidelines and proposals for determining the remote field J integral from experimental data agree with the numerical calculation of J from the stresses and distortions for large crack growth. With the stress, distortion and deformation fields available from the simulation with fine elementing in the ligament, the J concept for large ductile crack growth expanded by the multi-axiality parameter h is explained and the behaviour of other fracture parameters such as the crack tip opening (CTOD) and the crack opening angle (CTOA) for large crack growth are shown. (orig./DG)
Abstract (German)
Ueber das Risswiderstandsverhalten des Stahles StE 460 in seitengekerbten CT-25 und CCT-25-Proben nach dem J-Konzept jenseits des J-kontrollierten Bereichs bis zu einem Risswachstum von etwa 8 mm wird berichtet. Mit JR-Kurven gesteuerte numerische Simulationen des duktilen Risswachstums fuer EVZ-Modelle der Probengeometrien ermoeglichen eine Analyse, wie gut die Normen, Richtlinien und Vorschlaege fuer die Ermittlung des Fernfeld-J-Integrals aus Versuchdaten mit der numerischen Berechnung von J aus den Spannungen und Verzerrungen bei groesserem Risswachstum uebereinstimmen. Mit den aus der Simulation mit feiner Elementierung im Ligament zur Verfuegung stehenden Spannungs-, Verzerrungs- und Verformungsfeldern wird das um den Mehrachsigkeitsparameter h erweiterte J-Konzept fuer groesseres duktiles Risswachstum eroertert und das Verhalten anderer Bruchmechanikparameter wie die Rissspitzenoeffnung (CTOD) und der Rissoeffnungswinkel (CTOA) fuer groesseres Risswachstum dargestellt. (orig./DG)Additional details
Additional titles
- Original title (German)
- Grosses stabiles Risswachstum in Bruchmechanikproben
Publishing Information
- Imprint Title
- 18. MPA-Seminar. Safety and reliability of plant technology with special emphasis on nuclear technology. Vol. 1. Main focus: Safety aspects for long operational life and new reactor concepts. Papers 1-32
- Imprint Pagination
- [760 p.].
- Journal Page Range
- p. 17.1-17.25.
Conference
- Title
- Safety aspects for long operational life and new reactor concepts.
- Original Conference Title
- 18. MPA-Seminar: Sicherheit und Verfuegbarkeit in der Anlagentechnik -Langzeitsicherheit und Neue Reaktorkonzepte
- Acronym
- 18. MPA seminar on safety and reliability of plant technology
- Dates
- 8-9 Oct 1992.
- Place
- Stuttgart (Germany).
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 26044096
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference, Non-conventional Literature
- Descriptors DEI
- CHARPY TEST; COMPUTERIZED SIMULATION; CRACK PROPAGATION; FRACTURE MECHANICS; LOW ALLOY STEELS; NUMERICAL SOLUTION; STRESS INTENSITY FACTORS
- Descriptors DEC
- CARBON ADDITIONS; DESTRUCTIVE TESTING; IMPACT TESTS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS TESTING; MECHANICAL TESTS; MECHANICS; SIMULATION; STEELS; TESTING
Optional Information
- Notes
- Imprint:18. MPA-Seminar. Sicherheit und Verfuegbarkeit in der Anlagentechnik mit dem Schwerpunkt Kerntechnik. Bd. 1. Vorrangige Thematik: Langzeitsicherheit und neue Reaktorkonzepte. Vortraege 1-32.