Influence of E-beam irradiation on dielectric relaxation of recycled polypropylene

Full text: The dielectric relaxation connected with molecular groups and polymer chain mobility for un-irradiated and e-beam irradiated recycled polypropylene was investigated. It was studied films of samples produced from virgin (initial) and e- beam irradiated of the polymer granules (E-beam source with 5 MeV energy). The dielectric losses were measured with temperature increasing and decreasing regime. The losses were measured with E8-4 bridge help (the frequency is 1kH). Heating velocity was 2 grad/min. The dielectric losses did not appeared in minus temperature region for the initial polypropylene samples. The measurement in temperature increasing and decreasing shows that the relaxation peak at ∼ 35o C for un-irradiated and ∼70o C for irradiated polymer samples connected with macromolecular segments mobility with water molecular groups participation. The main relaxation peak (higher 100o C) shifts after e-beam irradiation is result of the cross-links formation. ) The peak connected with macromolecular segments mobility in polymer amorphous regions (β-relaxation process). In irradiated polypropylene on IR spectroscopy data oxygen molecular groups is increased. The molecular groupings form inter-molecular hydrogen bonds. The intermolecular bonds also hindered molecular groups and macromolecular mobility. The e-beam stimulated cross-links formation was confirmed by method of sol-gel analyses. The work was supported by STCU Fund (Project No 3009)