Ultraviolet-Visible Electroluminescence of a p-ZnO:As/n-Si Device Formed by the GaAs Interlayer Doping Method

Arsenic doped p-type ZnO films were grown on n-type silicon substrates using the GaAs interlayer doping method. Under our growth conditions the main doping element is arsenic, which was confirmed by x-ray photoelectroscopy. X-ray diffraction measurements revealed that the p-ZnO:As film was still in the (002) preferred orientation. The Hall test showed that the hole concentration of the p-ZnO:As film was 2.6 × 1017 cm−3. The acceptor level was located at 135 meV above the valance band maximum, according to the low-temperature photoluminescence results. We then fabricated a p-ZnO:As/n-Si heterojunction light-emitting device. Its current-voltage curve showed the typical rectifying behavior of a p—n diode. At forward current injections, the electroluminescence peaks, which cover the ultraviolet-to-visible region, could be clearly detected. (cross-disciplinary physics and related areas of science and technology)