Structure and phase composition of Al-Ce-Cu system alloys in range of quasi-binary Al-Al8CeCu4 section
Creators
- 1. Moskovskij Gosudarstvennyj Inst. Stali i Splavov (Tekhnologicheskij Univ.), Kafedra Metallovedeniya Tsvetnykh Metallov, Moscow (Russian Federation)
Description
The phase diagram of the Al-Cu-Ce system in the quasibinary section area of Al-Al8CeCu4 has been investigated by metallographic, thermal, micro-X-ray spectral and X-ray structural analyses. The parameters of the eutectic reaction L→(Al)+CeCu4Al8: T=610 Deg C were found out; the composition was 14% Cu and 7% Ce. This eutectics is of a disperse structure and the ternary compound contained is capable of fragmentation and spheroidizing in the heating process (starting from 540 Deg C). It was demonstrated that the area of optimal (Al)+CeCu4Al8 eutectics-based alloy compositions was within the narrow limits. That is related to the fact that at a comparatively little variation of the Cu:Ce=2 ratio solidus sharply decreases and, as a result, the crystallization interval considerably extends
Abstract (Russian)
Методами металлографического, термического, микрорентгеноспектрального и рентгеноструктурного анализов исследована фазовая диаграмма системы Al-Cu-Ce в области квазибинарного разреза Al-Аl8СеСu4. Установлены параметры эвтектической реакции L→(Al)+CeCu4Al8: Т=610 град С; состав - 14% Сu и 7% Се. Данная эвтектика имеет дисперсное строение, а входящее в нее тройное соединение способно к фрагментации и сфероидизации в процессе нагрева (начиная с 540 град С). Показано, что область оптимальных составов сплавов на основе эвтектики (Al)+CeCu4Al8 находится в узких пределах. Это связано с тем, что при сравнительно небольшом отклонении от соотношения Сu:Се=2 происходит резкое снижение солидуса и, как следствие, существенное расширение интервала кристаллизацииAdditional details
Additional titles
- Original title (Russian)
- Структура и фазовый состав сплавов системы Ал-Cе-Cу в области квазибинарного разреза Ал-Ал
Publishing Information
- Journal Title
- Izvestiya Vysshikh Uchebnykh Zavedenij. Tsvetnaya Metallurgiya
- Journal Issue
- no.1
- Journal Page Range
- p. 46-51
- ISSN
- 0021-3438
- CODEN
- IVUTAK
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 40088854
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ALUMINIUM BASE ALLOYS; CERIUM ALLOYS; CHEMICAL COMPOSITION; CONCENTRATION RATIO; COPPER ALLOYS; DIFFERENTIAL THERMAL ANALYSIS; EUTECTICS; METALLOGRAPHY; MICROSTRUCTURE; PHASE DIAGRAMS; TEMPERATURE RANGE 0400-1000 K; TERNARY ALLOY SYSTEMS; X-RAY DIFFRACTION
- Descriptors DEC
- ALLOY SYSTEMS; ALLOYS; ALUMINIUM ALLOYS; COHERENT SCATTERING; DIAGRAMS; DIFFRACTION; DIMENSIONLESS NUMBERS; INFORMATION; RARE EARTH ALLOYS; SCATTERING; TEMPERATURE RANGE; THERMAL ANALYSIS; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 10 refs., 6 figs., 2 tabs.