Comparison of Fatigue crack growth rate of Type 347 stainless steel with ASME and JSME models

In this study, the FCGR of 347SS was evaluated in modified PWR high temperature water conditions. The FCGRs of 347SS under modified pressurized-water conditions were measured by using compact-tension (CT) specimens at different levels of dissolved oxygen (DO), and it were compared with other models proposed by ASME and Japanese groups. Corrosion fatigue is main factor of environmental fatigue effect. Increase of DO level in water induced more corrosion damage, and it accelerated FCGR in PWR and FCGR of 347SS in PWR water condition was faster than reference curves in J-PWR and ASME draft code case derived by 304 and 316 stainless steel, but it was slower than J-BWR reference curve. Using J-BWR model for estimating the FCGR of 347SS under PWR might be conservative