Effect of HCl doping on optoelectrical and LPG sensing properties of nanostructured polyaniline thin films

Nanostructure Polyaniline thin films doped with 0.5 M, 0.7 M, and 1 M of HCL were synthesized by simple and inexpensive chemical oxidative polymerization technique at room temperature. All prepared thin films of Polyaniline were characterized by optical absorbance study by UV-visible spectroscopy. The absorbance spectrum of Polyaniline shows three fundamental peaks at 356, 419 and 820 nm with increase in absorption intensity. The electrical study shows magnitude of resistance of HCL doped Polyaniline is dependent on doping level. Furthermore, the thin film of Polyaniline was investigated by Scanning electron microscopy for surface morphology study. The SEM micrograph represents irregular granular morphology. In order to investigate LPG sensing properties, I-V characteristics of the Polyaniline films doped with 0.5 M, 0.7 M, and 1 M of HCL were recorded at room temperature in presence of air and 100 ppm of LPG. The observed values of sensitivity found to be 7.21%, 9.85% and 17.46 % for 0.5 M, 0.75 M, and 1.0 M of HCL doped Polyaniline thin films respectively