Pre-irradiation tests on U-Si alloys

Pre-irradiation tests of hardness, density, electrical resistivity, and corrosion resistance as well as metallographic and X-ray examinations were undertaken on U-Si core material, which had been co-extruded in Zr--2, in order that the effect of irradiation on alloys in the epsilon range could be assessed. In addition, a study of the epsilonization of arc-melted material was undertaken in order to rain familiarity with the epsilonization process and to obtain information on the corrosion behaviour of epsilonized material. Sheathed U-Si samples in the epsilonized and de-epsilonized conditions have been irradiated in the X-2 loop, with a water temperature of 275oC. The samples have been examined after 250 MWD/Tonne and show no dimensional change. (author)