Investigation on grain refinement and precipitation strengthening applied in high speed wire rod containing vanadium

To obtain necessary information for the simulation of high speed wire production process, the effect of grain refinement and precipitation strengthening on two high speed wire rod steels with different vanadium and nitrogen contents was investigated by continuous cooling transformation (CCT) characteristics. CCT curves were constructed by the dilatometer test and microscopic observation. Results showed that the formation of intra-granular ferrite (IGF) could refine grain remarkably and accelerate the ferrite transformation. Schedules for high speed wire production process focused on the effect of cooling rate. Ferrite grain was refined by increasing cooling rate and the formation of IGF. The microhardness calculation revealed that the steels were strengthened mostly by a combined effect of grain refinement and precipitation hardening. Degenerated pearlite was observed at lower transformation temperature and the fracture morphology changed from cementite lamellar to nanoscale cementite particle with increasing cooling rate. Based on the analysis above, an optimal schedule was applied and the microstructure and microhardness were improved