Recovery of deformed and hydrogen-charge palladium

Positron lifetime and Doppler-broadening studies made at 300 K have been used to investigate the interaction between interstitial hydrogen and lattice defects in deformed Pd. Specimens were charged with hydrogen at 300 K to levels up to 0.1%. The presence of hydrogen was found to have no effect on the recovery curves of Pd upon annealing to 4000C. By 4000C the values for both lifetime and Doppler-broadening for both cold worked and cold worked plus hydrogen were below the values obtained for annealed pure Pd. This can be interpreted as gaseous-impurity-trapped vacancies being present after the 12000C anneal, but being swept away by the dislocation microstructure recovery between 200 to 4000C