Neutron irradiation experiments on a pressure vessel steel for light-water reactors
Creators
- 1. Gesellschaft fuer Kernenergieverwertung in Schiffbau und Schiffahrt m.b.H., Geesthacht-Tesperhude (F.R. Germany). Inst. fuer Werkstofftechnologie
Description
Charpy-V-notch and tensile test specimens of the steel ASTM a 533 B were irradiated in the Material Testing Reactor FRG with three different neutron doses and tested in the Hot Cells. The results show a reduction of the shelf level and a progressive shift of the Nil Ductility Transition Temperature up to 1200C with increasing neutron doses for the impact specimens. The yield strength and the tensile strength increase and the elongation and reduction of area decrease progressively with higher fluences. Post-irradiation annealing of charpy specimens results in a more or less complete recovery, depending on the annealing temperature, annealing time and neutron dose. (orig.)
Abstract (German)
Die bei verschiedenen Dosen bestrahlten Kerbschlagbiege‐ und Zerreißproben zeigten nach der Prüfung eine Verminderung der Kerbschlagzähigkeit (absinkende Hochlage) und eine abgestufte Verschiebung der Sprödbruchübergangstemperatur, die bei der höchsten Dosis bis zu 120°C beträgt. Die Streckgrenze und die Bruchfestigkeit werden erhöht, während gleichzeitig die Dehnung und Brucheinschnürung abfallen. Erholungsglühversuche an bestrahlten Kerbschlagbiegeproben ergaben mit steigender Glühtemperatur zunehmende Erholungsraten. Der zweite Teil der Untersuchungen sieht eine Prüfung von Kerbschlagbiege‐ und Zerreißproben vor, die bei einer niedrigeren Temperatur bestrahlt wurden. Außerdem werden Fallgewichtsproben vom Typ P2 zur Ermittlung der NDT‐Temperatur und Bruchmechanikproben vom Typ WOL‐IX zur Bestimmung des Spannungsintensitätsfaktors K IC in Abhängigkeit von der Temperatur und der Bestrahlungsdosis bestrahlt.Additional details
Additional titles
- Original title (German)
- Bestrahlungsuntersuchungen an einem Druckbehaelterstahl fuer Leichtwasserreaktoren
Identifiers
Publishing Information
- Journal Title
- Materialwissenschaft und Werkstofftechnik
- Journal Volume
- 7
- Journal Issue
- 7
- Series
- Z. Werkstofftech.
- Journal Page Range
- 241-247
- ISSN
- 0933-5137
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 7270511
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ANNEALING; CHARPY TEST; DUCTILE-BRITTLE TRANSITIONS; EMBRITTLEMENT; EXPANSION; FRACTURES; IRRADIATION CAPSULES; NEUTRON BEAMS; NOTCHES; PHYSICAL RADIATION EFFECTS; PRESSURE VESSELS; RUPTURES; SHEAR; STEEL-ASTM-A533-B; TEMPERATURE DEPENDENCE; TENSILE PROPERTIES; TRANSITION TEMPERATURE; YIELD STRENGTH
- Descriptors DEC
- ALLOYS; BEAMS; CARBON ADDITIONS; CARBON STEELS; CONTAINERS; DESTRUCTIVE TESTING; FAILURES; HEAT TREATMENTS; IMPACT TESTS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS TESTING; MECHANICAL PROPERTIES; MECHANICAL TESTS; NUCLEON BEAMS; PARTICLE BEAMS; PHYSICAL PROPERTIES; RADIATION EFFECTS; STEELS; TESTING; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 21 figs.; 8 refs.; Updated automatically by Metadata and Full-Text Enrichment Agent