Comparison of welding induced residual stresses austenitic and ferritic steel weld joints

X-ray diffraction (XRD) is a well established technique for measurement of residual stresses in components and is being widely used. In XRD technique, the distance between the crystallographic planes (d spacing) is measured from peak position (2è) at various ø angles, where ø is the angle between the normal to the sample and the bisector of the incident and diffracted beam. From the slope of sin2ø vs. d spacing plot, the residual stresses are arrived by assuming a plane stress model. Welding induced residual stresses is of high importance as it is a major cause of failure in components. Surface compressive stresses improve the fatigue strength, whereas tensile residual stresses tend to decrease the fatigue strength. The present study compares the residual stresses that develop in 3 mm thick SS 316 and P91 TIG weld joints using the XRD technique. This study is aimed at understanding the influence of shrinkage during cooling and the effect of phase transformation induced volume changes on residual stress development in these two steels. While the first effect is predominant in the SS 316 weld, both the effects are present in the P91 welds. Stress measurements on SS 316 and P91 were carried out using Cr Kâ (λ-2.0840 Å) and Cr Ká (λ-2.2896 Å) radiations respectively. Typical 'M' type stress profile was observed across the weld centre line in both the welds. The variation and similarities between the longitudinal stress profiles observed in these two weld joints would be discussed. (author)